Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.18 g/cm³ |
| melt mass-flow rate | | ISO1133 | 7.3 g/10min |
| Shrinkage rate | | | 0.40to0.70 % |
| Water absorption rate | | ISO62 | 0.30 % |
| Average particle size | | | 600 µm |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | M-Scale | ISO2039-2 | 92 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| refractive index | | ISO489 | 1.490 |
| transmissivity | | ASTMD1003 | 92.0 % |
| Haze ratio | | ASTMD1003 | 0.40 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Hot filament ignition temperature | | IEC60695-2-13 | 650 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ISO178 | 3000 MPa |
| Bending stress | | ISO178 | 110 MPa |
| Tensile stress | | ISO527-2 | 80.0 MPa |
| Tensile strain | Break | ISO527-2 | 5.0 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 2.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 20 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/1A | 1.8 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ISO306/B | 102 °C |
| | ASTME831 | 7.1E-05 cm/cm/°C |
| Heat distortion temperature | | ISO75-2/B | 100 °C |
| Heat distortion temperature | | ISO75-2/A | 97.0 °C |
| vicat | | ISO306/A | 108 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.