PMMA LG702 LUCITE UK
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LUCITE UK/LG702 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ISO 180/1A | 1.8 kJ/m² | |
| Impact strength of simply supported beam without notch | ISO 179/1eU | 20 kJ/m² | |
| Charpy Notched Impact Strength | ISO 179/1eA | 2.0 kJ/m² |
| hardness | Test Condition | Test Method | LUCITE UK/LG702 |
|---|---|---|---|
| Rockwell hardness | M级 | ISO 2039-2 | 92 |
| Mechanical properties | Test Condition | Test Method | LUCITE UK/LG702 |
|---|---|---|---|
| tensile strength | ISO 527-2 | 80.0 MPa | |
| Tensile strain | 断裂 | ISO 527-2 | 5.0 % |
| Flexural modulus | ISO 178 | 3000 MPa | |
| bending strength | ISO 178 | 110 MPa |
| optical performance | Test Condition | Test Method | LUCITE UK/LG702 |
|---|---|---|---|
| transmissivity | ASTM D1003 | 92.0 % | |
| Haze ratio | ASTM D1003 | 0.40 % | |
| refractive index | ISO 489 | 1.490 |
| flammability | Test Condition | Test Method | LUCITE UK/LG702 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB | |
| Hot filament ignition temperature | IEC 60695-2-13 | 650 °C |
| physical property | Test Condition | Test Method | LUCITE UK/LG702 |
|---|---|---|---|
| Shrinkage rate | 0.40to0.70 % | ||
| melt mass-flow rate | 230°C/3.8kg | ISO 1133 | 7.3 g/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.30 % |
| Average particle size | 600 µm | ||
| density | ISO 1183 | 1.18 g/cm³ |
| Thermal performance | Test Condition | Test Method | LUCITE UK/LG702 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 100 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 97.0 °C | |
| Linear coefficient of thermal expansion | MD | ASTME831 | 7.1E-05 cm/cm/°C |
| vicat | -- | ISO 306/B | 102 °C |
| -- | ISO 306/A | 108 °C |