Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | g/cm³ | 1.35 -- |
| Shrinkage rate | | % | 1.1 -- |
| Water absorption rate | | % | 0.90 -- |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | | 120 105 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | | HB -- |
| Burning wire flammability index | | °C | 650 -- |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Break | MPa | 70.0 40.0 |
| elongation | Break | % | 8.0 12 |
| Flexural modulus | | MPa | 4000 2500 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Suspended wall beam without notch impact strength | | kJ/m² | >30 -- |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ohms | 1E+13 1E+11 |
| Volume resistivity | | ohms·cm | 1E+15 1E+11 |
| Compared to the Leakage Tracking Index (CTI) | | V | PLC 1 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | °C | 190 -- |
| Heat distortion temperature | | °C | 95.0 -- |
| vicat | | °C | 195 -- |
| melting temperature | | °C | 222 -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.