Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 POLYBEST 6 PD GK30 natural POLYMA Kunststoff GmbH & Co. KG
--
--
Filler, glass beads, 30%, filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | POLYMA Kunststoff GmbH & Co. KG/POLYBEST 6 PD GK30 natural |
|---|---|---|---|
| Suspended wall beam without notch impact strength | kJ/m² | >30 -- |
| hardness | Test Condition | Test Method | POLYMA Kunststoff GmbH & Co. KG/POLYBEST 6 PD GK30 natural |
|---|---|---|---|
| Rockwell hardness | R级 | 120 105 |
| Electrical performance | Test Condition | Test Method | POLYMA Kunststoff GmbH & Co. KG/POLYBEST 6 PD GK30 natural |
|---|---|---|---|
| Volume resistivity | ohms·cm | 1E+15 1E+11 | |
| Surface Resistivity | ohms | 1E+13 1E+11 | |
| Compared to the Leakage Tracking Index (CTI) | V | PLC 1 |
| Mechanical properties | Test Condition | Test Method | POLYMA Kunststoff GmbH & Co. KG/POLYBEST 6 PD GK30 natural |
|---|---|---|---|
| Flexural modulus | MPa | 4000 2500 | |
| elongation | 断裂 | % | 8.0 12 |
| tensile strength | 断裂 | MPa | 70.0 40.0 |
| flammability | Test Condition | Test Method | POLYMA Kunststoff GmbH & Co. KG/POLYBEST 6 PD GK30 natural |
|---|---|---|---|
| UL flame retardant rating | 1.6mm | HB -- | |
| Burning wire flammability index | °C | 650 -- |
| physical property | Test Condition | Test Method | POLYMA Kunststoff GmbH & Co. KG/POLYBEST 6 PD GK30 natural |
|---|---|---|---|
| Shrinkage rate | MD | % | 1.1 -- |
| density | g/cm³ | 1.35 -- | |
| Water absorption rate | 23°C,24hr | % | 0.90 -- |
| Thermal performance | Test Condition | Test Method | POLYMA Kunststoff GmbH & Co. KG/POLYBEST 6 PD GK30 natural |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | °C | 190 -- |
| melting temperature | °C | 222 -- | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | °C | 95.0 -- |
| vicat | °C | 195 -- |