PP STATEX® 18
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792 | 0.988 g/cm³ | |
| Water absorption rate | Saturation | ASTM D570 | 0.010 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 | |
| Limiting Oxygen Index | ASTM D2863 | 28 % |
| film | Test Condition | Test Method | Test Result |
|---|---|---|---|
| film thickness | 360to560 µm | ||
| tensile strength | ASTM D882 | 33.1 MPa | |
| ASTM D882 | 24.8 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot wire ignition (HWI) | UL 746 | PLC 4 sec | |
| dielectric strength | ASTM D149 | 27500 V | |
| StaticDecay | ASTM D257 | <2.0 sec | |
| Surface Resistivity | ASTM D257 | 1.0E+10到1.0E+12 ohms | |
| Volume resistivity | ASTM D257 | 1.5E+17 ohms·cm | |
| dielectric strength | ASTM D149 | 60 kV/mm | |
| dielectric constant | ASTM D150 | 2.30 | |
| Dissipation Factor | ASTM D150 | 9E-04 | |
| Compared to the Leakage Tracking Index (CTI) | ASTM D3638 | PLC 0 | |
| High arc combustion index (HAI) | UL 746 | PLC 3 | |
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | mm/min |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| RTI | UL 746 | 100 °C | |
| Hot deformation temperature (HDT) | ASTM D648 | 106 °C | |
| RTI Elec | UL 746 | 100 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.