Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ISO62 | 0.31 % |
| density | | ISO1183 | 1.41 g/cm³ |
| Shrinkage rate | | ISO294-4 | 0.60to0.80 % |
| Shrinkage rate | | ISO294-4 | 0.30to0.50 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| UL flame retardant rating | | UL94 | HB |
| UL flame retardant rating | | UL94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Dimensional Stability | | | 61.0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strain | | ISO527-2/5 | 5.5 % |
| Tensile strain | | ISO527-2/5 | 6.0 % |
| Tensile strain | | ISO527-2/5 | 5.0 % |
| Tensile modulus | | ISO527-2/1 | 10500 MPa |
| Tensile modulus | | ISO527-2/1 | 8500 MPa |
| Tensile modulus | | ISO527-2/1 | 5800 MPa |
| Tensile modulus | | ISO527-2/1 | 4600 MPa |
| Tensile modulus | | ISO527-2/1 | 3700 MPa |
| Tensile stress | | ISO527-2/5 | 175 MPa |
| Tensile stress | | ISO527-2/5 | 130 MPa |
| Tensile stress | | ISO527-2/5 | 100 MPa |
| Tensile stress | | ISO527-2/5 | 90.0 MPa |
| Tensile stress | | ISO527-2/5 | 80.0 MPa |
| Tensile strain | | ISO527-2/5 | 3.0 % |
| Tensile strain | | ISO527-2/5 | 3.8 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 10 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 75 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/B | 220 °C |
| | ISO75-2/A | 205 °C |
| Continuous use temperature | | | 130 °C |
| vicat | | ISO306/B50 | 215 °C |
| | ISO11359-2 | 1.2E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare