Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 Latamid 6 H2 G/35 LATI S.p.A.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LATI S.p.A./Latamid 6 H2 G/35 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 10 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 75 kJ/m² |
| Supplementary Information | Test Condition | Test Method | LATI S.p.A./Latamid 6 H2 G/35 |
|---|---|---|---|
| dimensional stability | 61.0 |
| Mechanical properties | Test Condition | Test Method | LATI S.p.A./Latamid 6 H2 G/35 |
|---|---|---|---|
| tensile strength | 断裂,90°C | ISO 527-2/5 | 100 MPa |
| Tensile strain | 断裂,23°C | ISO 527-2/5 | 3.0 % |
| tensile strength | 断裂,120°C | ISO 527-2/5 | 90.0 MPa |
| 断裂,150°C | ISO 527-2/5 | 80.0 MPa | |
| Tensile modulus | 90°C | ISO 527-2/1 | 5800 MPa |
| 23°C | ISO 527-2/1 | 10500 MPa | |
| Tensile strain | 断裂,120°C | ISO 527-2/5 | 5.5 % |
| Tensile modulus | 60°C | ISO 527-2/1 | 8500 MPa |
| Tensile strain | 断裂,150°C | ISO 527-2/5 | 6.0 % |
| tensile strength | 断裂,60°C | ISO 527-2/5 | 130 MPa |
| 断裂,23°C | ISO 527-2/5 | 175 MPa | |
| Tensile modulus | 120°C | ISO 527-2/1 | 4600 MPa |
| 150°C | ISO 527-2/1 | 3700 MPa | |
| Tensile strain | 断裂,60°C | ISO 527-2/5 | 3.8 % |
| 断裂,90°C | ISO 527-2/5 | 5.0 % |
| flammability | Test Condition | Test Method | LATI S.p.A./Latamid 6 H2 G/35 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | HB |
| 3.0mm | UL 94 | HB | |
| 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | LATI S.p.A./Latamid 6 H2 G/35 |
|---|---|---|---|
| Shrinkage rate | MD:2.00mm | ISO 294-4 | 0.30to0.50 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.31 % |
| density | ISO 1183 | 1.41 g/cm³ | |
| Shrinkage rate | TD:2.00mm | ISO 294-4 | 0.60to0.80 % |
| Thermal performance | Test Condition | Test Method | LATI S.p.A./Latamid 6 H2 G/35 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 220 °C |
| vicat | ISO 306/B50 | 215 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 205 °C |
| Continuous use temperature | 130 °C | ||
| Linear coefficient of thermal expansion | MD：30到100°C | ISO 11359-2 | 1.2E-05 cm/cm/°C |