| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.15 g/cm³ |
| melt mass-flow rate | | ISO1133 | 25 g/10min |
| Water absorption rate | | ISO62 | 0.20 % |
| Humidity-Pellets | | ISO1110 | 0.20 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO868 | 80 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| burning rate | | FMVSS302 | <100 mm/min |
| UL flame retardant rating | | UL94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO180 | 38 kJ/m² |
| | ISO180 | 无断裂 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2 | 2200 MPa |
| Tensile stress | | ISO527-2 | 50.0 MPa |
| Tensile strain | Break | ISO527-2 | >50 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | <1.0E+16 ohms |
| dielectric strength | | IEC60243-1 | 35 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/B | 120 °C |
| | ISO75-2/A | 100 °C |
| vicat | | ISO306 | 125 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.