PC Iupilon® LCH2315

Properties:
Filler
carbon fiber reinforced material
15%
filler by weight
Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
density		ISO 1183	1.37 g/cm³
melt mass-flow rate		ISO 1133	1.7 g/10min
Melt volume flow rate		ISO 1133	1.30 cm³/10min
Shrinkage rate			0.20to0.40 %
	Shrinkage rate			0.050to0.20 %
	Shrinkage rate	Shrinkage rate			0.080 %

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	HB

Mechanical properties	Test Condition	Test Method	Test Result
Tensile strain	Break	ISO 527-2	2.1 %
Flexural modulus		ISO 178	9400 MPa
bending strength		ISO 178	180 MPa
Tensile modulus		ISO 527-2	10000 MPa
tensile strength	Break	ISO 527-2	105 MPa

Impact resistance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength		ISO 179	8.0 kJ/m²
Impact strength of simply supported beam without notch		ISO 179	35 kJ/m²

Thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion		ISO 11359-2	1.4E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion		ISO 11359-2	6.5E-05 cm/cm/°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.