PC Iupilon® LCH2315 Mitsubishi Chemical Corporation
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Mitsubishi Chemical Corporation/Iupilon® LCH2315 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 8.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 35 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Mitsubishi Chemical Corporation/Iupilon® LCH2315 |
|---|---|---|---|
| Tensile strain | 断裂 | ISO 527-2 | 2.1 % |
| Tensile modulus | ISO 527-2 | 10000 MPa | |
| tensile strength | 断裂 | ISO 527-2 | 105 MPa |
| Flexural modulus | ISO 178 | 9400 MPa | |
| bending strength | ISO 178 | 180 MPa |
| flammability | Test Condition | Test Method | Mitsubishi Chemical Corporation/Iupilon® LCH2315 |
|---|---|---|---|
| UL flame retardant rating | 0.400mm | UL 94 | HB |
| physical property | Test Condition | Test Method | Mitsubishi Chemical Corporation/Iupilon® LCH2315 |
|---|---|---|---|
| Shrinkage rate | TD:3.20mm | 0.20to0.40 % | |
| 吸水率(饱和,23°C) | 0.080 % | ||
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 1.30 cm³/10min |
| Shrinkage rate | MD:3.20mm | 0.050to0.20 % | |
| density | ISO 1183 | 1.37 g/cm³ | |
| melt mass-flow rate | 300°C/1.2kg | ISO 1133 | 1.7 g/10min |
| Thermal performance | Test Condition | Test Method | Mitsubishi Chemical Corporation/Iupilon® LCH2315 |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.4E-05 cm/cm/°C |
| TD | ISO 11359-2 | 6.5E-05 cm/cm/°C |