ABS

ABS TAITALAC® 1000T TAIDA TAIWAN

Properties:
High glossHigh mobilityFatigue resistanceModerate impact resistanc
Usages:
batteryElectrical enclosureElectrical appliancesTV casingfurnitureToyFootwearbatteryElectrical enclosureElectrical appliancesTV casingfurnitureToyFootwear
Certificates:
ULTDSTDS_ISOUL
Compare View Prices

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23°C,6.35mm	ASTM D256	230 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C,3.18mm	ASTM D256	260 J/m

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.6mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
bending strength	Yield,23°C	ASTM D790	68.9 Mpa
Bending modulus	23°C	ASTM D790	2340 Mpa
Bending modulus	Bending modulus	23℃	ASTM D790	2340 Mpa
elongation	Break, 23℃, 3.18 mm	ASTM D638	30 %
tensile strength	Break, 23℃, 3.18 mm	ASTM D638	35.2 Mpa
tensile strength	tensile strength	Yield, 23℃, 3.18 mm	ASTM D638	40 Mpa
Rockwell hardness	R-Scale, 23℃	ASTM D785	110
Impact strength of cantilever beam gap	23℃, 6.35 mm	ASTM D256	230 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23℃, 3.18 mm	ASTM D256	260 J/m
bending strength	Yield, 23℃	ASTM D790	68.9 Mpa
tensile strength	Yield,23°C,3.18mm	ASTM D638	40.0 Mpa
tensile strength	tensile strength	Break,23°C,3.18mm	ASTM D638	35.2 Mpa
elongation	Break,23°C,3.18mm	ASTM D638	30 %

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8MPa,Annealed,12.7mm	ASTM D648	86.0 °C
Vicat softening temperature		ASTM D15255	103 °C
RTI Elec	1.6mm	UL 746	60.0 °C
UL flame retardant rating	1.59 mm	UL 94	HB
Hot wire ignition	1.57 mm	UL 746	sec
High voltage arc tracing rate	1.57 mm	UL 746	mm/min
High arc combustion index	1.57 mm	UL 746
Vicat softening temperature		ASTM D1525	103 °C
Hot deformation temperature	1.8 MPa, Annealed, 12.7 mm	ASTM D648	86 °C
RTI Imp	1.6mm	UL 746	60.0 °C
RTI Str	1.6mm	UL 746	60.0 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Saturation	ASTM D570	< 0.30 %
Shrinkage rate	MD	ASTM D955	< 0.40 %
melt mass-flow rate	220℃/10.0 kg	ASTM D1238	18 g/10 min
melt mass-flow rate	melt mass-flow rate	200℃/5.0 kg	ASTM D1238	1.8 g/10 min
density		ASTM D792	1.03 g/cm³
density	density		ASTM D792	1.03 g/cm³
melt mass-flow rate	200°C/5.0kg	ASTM D1238	1.8 g/10min
melt mass-flow rate	melt mass-flow rate	220°C/10.0kg	ASTM D1238	18 g/10min
Shrinkage rate	MD	ASTM D955	<0.40 %
Water absorption rate	Saturation	ASTM D570	<0.30 %

Electrical performance	Test Condition	Test Method	Test Result
High arc combustion index	1.57mm	UL 746
High voltage arc tracing rate	1.57mm	UL 746	mm/min
Hot wire ignition	1.57mm	UL 746	sec

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Sale,23°C	ASTM D785	110

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

ABS TAITALAC® 1000T TAIDA TAIWAN

Technical Data Sheet