Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS 1000T TAIDA TAIWAN
TAITALAC®
battery、Electrical enclosure、Electrical appliances、TV casing、furniture、Toy、Footwear、battery、Electrical enclosure、Electrical appliances、TV casing、furniture、Toy、Footwear
High gloss、High mobility、Fatigue resistance、Moderate impact resistanc
UL
TDS
TDS_ISO
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TAIDA TAIWAN/1000T |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,6.35mm | ASTMD256 | 230 J/m |
| 23°C,3.18mm | ASTMD256 | 260 J/m |
| hardness | Test Condition | Test Method | TAIDA TAIWAN/1000T |
|---|---|---|---|
| Rockwell hardness | R计秤,23°C | ASTMD785 | 110 |
| Mechanical properties | Test Condition | Test Method | TAIDA TAIWAN/1000T |
|---|---|---|---|
| tensile strength | 屈服,23°C,3.18mm | ASTMD638 | 40.0 Mpa |
| 断裂, 23℃, 3.18 mm | ASTM D638 | 35.2 Mpa | |
| 屈服, 23℃, 3.18 mm | ASTM D638 | 40 Mpa | |
| Flexural modulus | 23℃ | ASTM D790 | 2340 Mpa |
| elongation | 断裂, 23℃, 3.18 mm | ASTM D638 | 30 % |
| Tensile strength 2 | Break,23°C,3.18mm | ASTMD638 | 35.2 Mpa |
| elongation | 断裂,23°C,3.18mm | ASTMD638 | 30 % |
| Flexural modulus | 23°C | ASTMD790 | 2340 Mpa |
| Impact strength of cantilever beam gap | 23℃, 6.35 mm | ASTM D256 | 230 J/m |
| bending strength | 屈服,23°C | ASTMD790 | 68.9 Mpa |
| Impact strength of cantilever beam gap | 23℃, 3.18 mm | ASTM D256 | 260 J/m |
| bending strength | 屈服, 23℃ | ASTM D790 | 68.9 Mpa |
| Rockwell hardness | R 级, 23℃ | ASTM D785 | 110 |
| Electrical performance | Test Condition | Test Method | TAIDA TAIWAN/1000T |
|---|---|---|---|
| High arc combustion index (HAI) | 1.57mm | UL746 | 200 |
| High voltage arc ignition resistance index | 1.57mm | UL746 | 0.00 mm/min |
| Hot-wireIgnition | 1.57mm | UL746 | 17 sec |
| flammability | Test Condition | Test Method | TAIDA TAIWAN/1000T |
|---|---|---|---|
| FlameRating | 1.6mm | UL94 | HB |
| physical property | Test Condition | Test Method | TAIDA TAIWAN/1000T |
|---|---|---|---|
| melt mass-flow rate | 200℃/5.0 kg | ASTM D1238 | 1.8 g/10 min |
| Shrinkage rate | MD | ASTM D955 | < 0.40 % |
| Water absorption rate | 饱和 | ASTM D570 | < 0.30 % |
| melt mass-flow rate | 200°C/5.0kg | ASTMD1238 | 1.8 g/10min |
| density | ASTMD792 | 1.03 g/cm³ | |
| Shrinkage rate | MD | ASTMD955 | <0.40 % |
| density | ASTM D792 | 1.03 g/cm³ | |
| melt mass-flow rate | 220℃/10.0 kg | ASTM D1238 | 18 g/10 min |
| 220°C/10.0kg | ASTMD1238 | 18 g/10min | |
| Water absorption rate | 饱和 | ASTMD570 | <0.30 % |
| Thermal performance | Test Condition | Test Method | TAIDA TAIWAN/1000T |
|---|---|---|---|
| 1.8 MPa, 退火, 12.7 mm | ASTM D648 | 86 °C | |
| vicat | ASTM D1525 | 103 °C | |
| High arc combustion index (HAI) | 1.57 mm | UL 746 | 200 |
| RTI Elec | 1.6mm | UL746 | 60.0 °C |
| High Voltage Arc Traceability Rate (HVTR) | 1.57 mm | UL 746 | 0.00 mm/min |
| ASTMD15255 | 103 °C | ||
| RTI Str | 1.6mm | UL746 | 60.0 °C |
| Hot wire ignition (HWI) | 1.57 mm | UL 746 | 17 sec |
| 1.8MPa,Annealed,12.7mm | ASTMD648 | 86.0 °C | |
| RTI Imp | 1.6mm | UL746 | 60.0 °C |
| UL flame retardant rating | 1.59 mm | UL 94 | HB |