Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D1238 | 11 g/10min |
| Water absorption rate | | ASTM D570 | 0.070 % |
| Water absorption rate | | ISO 62 | 0.070 % |
| Melt volume flow rate | | ISO 1133 | 11.0 cm³/10min |
| Shrinkage rate | | ASTM D955 | 0.65 % |
| Shrinkage rate | | ISO 294-4 | 0.30to1.0 % |
| density | | ASTM D792 | 1.01 g/cm³ |
| density | | ISO 1183 | 1.01 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTM D2240 | 68 |
| Shore hardness | | ISO 868 | 68 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| refractive index | | ASTM D542 | 1.575 |
| refractive index | | ISO 489 | 1.575 |
| transmissivity | | ASTM D1003 | 90.0 % |
| Haze ratio | | ASTM D1003 | 1.5 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179 | NoBreak |
| Impact strength of cantilever beam gap | | ASTM D256 | 43 J/m |
| Impact strength of cantilever beam gap | | ISO 180/A | 3.0 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/A | 4.0 kJ/m² |
| Dart impact | | ASTM D3763 | 11.0 J |
| Dart impact | | ASTM D3763 | 22.1 J |
| Charpy Notched Impact Strength | | ISO 179 | 4.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| elongation | | ASTM D638 | 250 % |
| Nominal tensile fracture strain | | ISO 527-2 | 160 % |
| Tensile creep modulus | | ISO 899-1 | 1300 MPa |
| Tensile creep modulus | | ISO 899-1 | 790 MPa |
| Tensile modulus | | ASTM D638 | 1310 MPa |
| Tensile modulus | | ISO 527-2 | 1500 MPa |
| tensile strength | | ASTM D638 | 26.0 MPa |
| tensile strength | | ISO 527-2 | 26.0 MPa |
| Tensile strain | | ISO 527-2 | 2.3 % |
| Flexural modulus | | ASTM D790 | 1170 MPa |
| Flexural modulus | | ISO 178 | 1700 MPa |
| bending strength | | ASTM D790 | 31.0 MPa |
| bending strength | | ISO 178 | 40.0 MPa |
| film | Test Condition | Test Method | Test Result |
|---|
| elongation | Break | ASTM D882 | 260 % |
| Tensile strain | | ASTM D882 | 100 % |
| elongation | Break | ISO 527-3 | 160 % |
| Elmendorf tear strength | | ASTM D1922 | 250 g |
| Elmendorf tear strength | | ASTM D1922 | 240 g |
| OTr | | ASTM D3985 | 120000 cm³/m²/24hr |
| Water Vapor Transmission Rate | | ASTMF1249 | 700 g/m²/24hr |
| Tensile modulus | | ASTM D882 | 1320 MPa |
| Tensile modulus | | ASTM D882 | 1180 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric constant | | IEC 60250 | 2.50 |
| Dissipation Factor | | IEC 60250 | 3E-04 |
| Dissipation Factor | | IEC 60250 | 8E-04 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Volume resistivity | | IEC 60093 | >1.0E+15 ohms·cm |
| dielectric constant | | ASTM D150 | 2.50 |
| Surface Resistivity | | ASTM D257 | >1.0E+14 ohms |
| Surface Resistivity | | IEC 60093 | 1E+15 ohms |
| Volume resistivity | | ASTM D257 | >1.0E+15 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 76.7 °C |
| Heat distortion temperature | | ISO 75-2/B | 75.0 °C |
| Heat distortion temperature | | ASTM D648 | 70.0 °C |
| Heat distortion temperature | | ISO 75-2/A | 65.0 °C |
| vicat | | ASTM D15254 | 85.6 °C |
| vicat | | ISO 306/A50 | 83.0 °C |
| vicat | | ISO 306/B50 | 59.0 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 1.3E-04 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 6.0E-5to9.0E-5 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.