SBC Styrolux® 684D INEOS Barex
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodINEOS Barex/Styrolux® 684D
Charpy Notched Impact Strength23°CISO 1794.0 kJ/m²
Impact strength of cantilever beam gap23°CASTM D25643 J/m
Dart impactPeakforceASTM D376311.0 J
Impact strength of simply supported beam without notch23°CISO 179NoBreak
Dart impactTotalenergyASTM D376322.1 J
Impact strength of cantilever beam gap23°CISO 180/A4.0 kJ/m²
-30°CISO 180/A3.0 kJ/m²
hardnessTest ConditionTest MethodINEOS Barex/Styrolux® 684D
Shore hardness邵氏DASTM D224068
邵氏DISO 86868
filmTest ConditionTest MethodINEOS Barex/Styrolux® 684D
Elmendorf tear strengthMDASTM D1922250 g
Tensile modulusTDASTM D8821180 MPa
elongation断裂ASTM D882260 %
OTr23°C,0%RHASTM D3985120000 cm³/m²/24hr
elongation断裂ISO 527-3160 %
Tensile strainBreakASTM D882100 %
Tensile modulusMDASTM D8821320 MPa
Elmendorf tear strengthTDASTM D1922240 g
Water Vapor Transmission Rate23°CASTMF1249700 g/m²/24hr
Mechanical propertiesTest ConditionTest MethodINEOS Barex/Styrolux® 684D
tensile strength 屈服,23°CISO 527-226.0 MPa
Tensile modulusISO 527-21500 MPa
Flexural modulusISO 1781700 MPa
bending strengthASTM D79031.0 MPa
ISO 17840.0 MPa
Tensile modulusASTM D6381310 MPa
Flexural modulusASTM D7901170 MPa
Tensile creep modulus1hrISO 899-11300 MPa
Tensile strain屈服,23°CISO 527-22.3 %
Nominal tensile fracture strain23°CISO 527-2160 %
Tensile creep modulus1000hrISO 899-1790 MPa
tensile strength 屈服,23°CASTM D63826.0 MPa
elongation断裂,23°CASTM D638250 %
Electrical performanceTest ConditionTest MethodINEOS Barex/Styrolux® 684D
Compared to the Leakage Tracking Index (CTI)IEC 60112PLC 0
dielectric constant100HzIEC 602502.50
Volume resistivityASTM D257>1.0E+15 ohms·cm
IEC 60093>1.0E+15 ohms·cm
Surface ResistivityASTM D257>1.0E+14 ohms
Dissipation Factor100HzIEC 602503E-04
dielectric constant1.00mm,1MHzASTM D1502.50
Surface ResistivityIEC 600931E+15 ohms
Dissipation Factor1MHzIEC 602508E-04
optical performance Test ConditionTest MethodINEOS Barex/Styrolux® 684D
transmissivity550nmASTM D100390.0 %
refractive indexASTM D5421.575
Haze ratioASTM D10031.5 %
refractive indexISO 4891.575
physical property Test ConditionTest MethodINEOS Barex/Styrolux® 684D
melt mass-flow rate200°C/5.0kgASTM D123811 g/10min
Shrinkage rateMDASTM D9550.65 %
Water absorption rate饱和,23°CASTM D5700.070 %
Shrinkage rateISO 294-40.30to1.0 %
Water absorption rate饱和,23°CISO 620.070 %
densityASTM D7921.01 g/cm³
ISO 11831.01 g/cm³
Melt volume flow rate200°C/5.0kgISO 113311.0 cm³/10min
Thermal performanceTest ConditionTest MethodINEOS Barex/Styrolux® 684D
Heat distortion temperature1.8MPa,未退火，HDTASTM D64870.0 °C
0.45MPa,未退火，HDTASTM D64876.7 °C
vicatASTM D1525485.6 °C
Heat distortion temperature1.8MPa,Annealed，HDTISO 75-2/A65.0 °C
vicat--ISO 306/A5083.0 °C
--ISO 306/B5059.0 °C
Linear coefficient of thermal expansionMDASTM D6961.3E-04 cm/cm/°C
MDISO 11359-26.0E-5to9.0E-5 cm/cm/°C
Heat distortion temperature0.45MPa,Annealed，HDTISO 75-2/B75.0 °C