PA LNP™ THERMOTUF™ V1000UXC compound
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | ASTM D570 | 0.60 % | |
| density | ASTM D792 | 1.07 g/cm³ | |
| ISO 1183 | 1.08 g/cm³ | ||
| Shrinkage rate | ASTM D955 | 2.1to2.3 % | |
| ASTM D955 | 2.5to2.7 % | ||
| Water absorption rate | ISO 62 | 1.0 % | |
| Shrinkage rate | ISO 294-4 | 2.6 % | |
| ISO 294-4 | 2.2 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dart impact | ISO 6603-2 | 49.4 J | |
| Suspended wall beam without notch impact strength | ASTMD4812 | 无断裂 | |
| Dart impact | ASTM D3763 | 49.8 J |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flexural modulus | ISO 178 | 1700 MPa | |
| bending strength | ASTM D790 | 55.2 MPa | |
| ISO 178 | 53.0 MPa | ||
| elongation | ASTM D638 | 57 % | |
| Yield | ISO 527-2/5 | 150 % | |
| ASTM D638 | 85 % | ||
| Tensile modulus | ASTM D638 | 1710 MPa | |
| ISO 527-2/1 | 1650 MPa | ||
| tensile strength | ASTM D638 | 39.0 MPa | |
| Yield | ISO 527-2/5 | 41.0 MPa | |
| ASTM D638 | 39.0 MPa | ||
| Break | ISO 527-2/5 | 41.0 MPa | |
| elongation | Break | ISO 527-2/5 | 170 % |
| Flexural modulus | ASTM D790 | 2070 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear coefficient of thermal expansion | ASTME831 | 1.4E-04 cm/cm/°C | |
| ISO 11359-2 | 1.3E-04 cm/cm/°C | ||
| ASTME831 | 1.3E-04 cm/cm/°C | ||
| Heat distortion temperature | ASTM D648 | 192 °C | |
| ISO 75-2/Bf | 150 °C | ||
| ASTM D648 | 193 °C | ||
| ISO 75-2/Af | 147 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.