Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA LNP™ THERMOTUF™ V1000UXC compound SABIC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC/LNP™ THERMOTUF™ V1000UXC compound |
|---|---|---|---|
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 49.8 J |
| Suspended wall beam without notch impact strength | 23°C | ASTMD4812 | 无断裂 |
| Dart impact | -- | ISO 6603-2 | 49.4 J |
| Mechanical properties | Test Condition | Test Method | SABIC/LNP™ THERMOTUF™ V1000UXC compound |
|---|---|---|---|
| bending strength | -- | ASTM D790 | 55.2 MPa |
| tensile strength | 屈服3 | ASTM D638 | 39.0 MPa |
| elongation | 断裂3 | ASTM D638 | 85 % |
| tensile strength | 屈服 | ISO 527-2/5 | 41.0 MPa |
| Tensile modulus | -- | ISO 527-2/1 | 1650 MPa |
| Flexural modulus | -- | ASTM D790 | 2070 MPa |
| elongation | 屈服 | ISO 527-2/5 | 150 % |
| tensile strength | 断裂 | ISO 527-2/5 | 41.0 MPa |
| elongation | 屈服3 | ASTM D638 | 57 % |
| Flexural modulus | -- | ISO 178 | 1700 MPa |
| bending strength | -- | ISO 178 | 53.0 MPa |
| tensile strength | 断裂3 | ASTM D638 | 39.0 MPa |
| elongation | 断裂 | ISO 527-2/5 | 170 % |
| Tensile modulus | --2 | ASTM D638 | 1710 MPa |
| physical property | Test Condition | Test Method | SABIC/LNP™ THERMOTUF™ V1000UXC compound |
|---|---|---|---|
| Shrinkage rate | MD:24小时 | ISO 294-4 | 2.2 % |
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.60 % |
| Shrinkage rate | TD:24小时 | ASTM D955 | 2.5to2.7 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 1.0 % |
| density | -- | ASTM D792 | 1.07 g/cm³ |
| Shrinkage rate | MD:24小时 | ASTM D955 | 2.1to2.3 % |
| TD:24小时 | ISO 294-4 | 2.6 % | |
| density | -- | ISO 1183 | 1.08 g/cm³ |
| Thermal performance | Test Condition | Test Method | SABIC/LNP™ THERMOTUF™ V1000UXC compound |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,64.0mm跨距4，HDT | ISO 75-2/Af | 147 °C |
| Linear coefficient of thermal expansion | MD:-40到40°C | ISO 11359-2 | 1.3E-04 cm/cm/°C |
| TD:-40到40°C | ASTME831 | 1.3E-04 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 192 °C |
| 0.45MPa,未退火,64.0mm跨距4，HDT | ISO 75-2/Bf | 150 °C | |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 193 °C | |
| Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 1.4E-04 cm/cm/°C |