Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.05 g/cm³ |
| density | | ISO 1183 | 1.05 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 7.0 g/10min |
| melt mass-flow rate | | ISO 1133 | 7.0 g/10min |
| Shrinkage rate | | ASTM D955 | 0.50 % |
| Shrinkage rate | | ASTM D955 | 0.50 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTM D785 | 85 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| burning rate | | SAEJ369 | 45 mm/min |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/eA | 7.0 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/eA | 15 kJ/m² |
| Impact strength of cantilever beam gap | | ASTM D256 | 170 J/m |
| Dart impact | | ASTM D5420 | 4.00 J |
| Dart impact | | ASTM D5420 | 15.0 J |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2/1 | 2000 MPa |
| tensile strength | | ASTM D638 | 36.0 MPa |
| tensile strength | Yield | ISO 527-2/50 | 35.0 MPa |
| Flexural modulus | | ASTM D790 | 2100 MPa |
| Flexural modulus | | ISO 178 | 2200 MPa |
| bending strength | | ASTM D790 | 62.0 MPa |
| bending strength | | ISO 178 | 58.0 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 80.0 °C |
| vicat | | ISO 306/B50 | 86.0 °C |
| Heat distortion temperature | | ISO 75-2/B | 90.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.