ABS VYTEEN ABS 2904 Lavergne Group
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | Lavergne Group/VYTEEN ABS 2904 |
---|---|---|---|
Impact strength of cantilever beam gap | 23°C | ASTM D256 | 170 J/m |
Charpy Notched Impact Strength | -30°C | ISO 179/eA | 7.0 kJ/m² |
23°C | ISO 179/eA | 15 kJ/m² | |
Dart impact | 23°C | ASTM D5420 | 15.0 J |
-29°C | ASTM D5420 | 4.00 J |
hardness | Test Condition | Test Method | Lavergne Group/VYTEEN ABS 2904 |
---|---|---|---|
Rockwell hardness | R级 | ASTM D785 | 85 |
Mechanical properties | Test Condition | Test Method | Lavergne Group/VYTEEN ABS 2904 |
---|---|---|---|
tensile strength | 屈服2 | ASTM D638 | 36.0 MPa |
bending strength | --3 | ASTM D790 | 62.0 MPa |
Flexural modulus | --3 | ASTM D790 | 2100 MPa |
--4 | ISO 178 | 2200 MPa | |
bending strength | --4 | ISO 178 | 58.0 MPa |
Tensile modulus | ISO 527-2/1 | 2000 MPa | |
tensile strength | 屈服 | ISO 527-2/50 | 35.0 MPa |
flammability | Test Condition | Test Method | Lavergne Group/VYTEEN ABS 2904 |
---|---|---|---|
burning rate | SAEJ369 | 45 mm/min |
physical property | Test Condition | Test Method | Lavergne Group/VYTEEN ABS 2904 |
---|---|---|---|
density | 23°C | ISO 1183 | 1.05 g/cm³ |
melt mass-flow rate | 200°C/5.0kg | ASTM D1238 | 7.0 g/10min |
Shrinkage rate | MD | ASTM D955 | 0.50 % |
melt mass-flow rate | 230°C/3.8kg | ISO 1133 | 7.0 g/10min |
density | -- | ASTM D792 | 1.05 g/cm³ |
Shrinkage rate | TD | ASTM D955 | 0.50 % |
Thermal performance | Test Condition | Test Method | Lavergne Group/VYTEEN ABS 2904 |
---|---|---|---|
Heat distortion temperature | 1.8MPa,未退火,HDT | ASTM D648 | 80.0 °C |
0.45MPa,未退火,HDT | ISO 75-2/B | 90.0 °C | |
vicat | ISO 306/B50 | 86.0 °C |