POM 500TL NC010 Dow DuPont

Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
density		ISO 1183	1.43 g/cm³
Water absorption rate		ISO 62	0.17 %
Shrinkage rate		ISO 294-4	1.9 %
Shrinkage rate	Shrinkage rate			1.9 %
melt mass-flow rate		ISO 1133	14 g/10min

Mechanical properties	Test Condition	Test Method	Test Result
Tensile strain		ISO 527-1/-2	14 %
elongation	Break	ISO 527-1/-2	20 %
Tensile modulus		ISO 527-1/-2	3300 MPa
Flexural modulus		ISO 178	3000 MPa
Impact strength of cantilever beam gap		ISO 180/1A	6 KJ/㎡
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ISO 180/1A	6 KJ/㎡
Charpy Notched Impact Strength		ISO 179/leA	5 KJ/㎡
Impact strength of simply supported beam without notch		ISO 179/leU	160 KJ/㎡
Tensile stress		ISO 527-1/-2	71 MPa

Other performance	Test Condition	Test Method	Test Result
Melting temperature range			210-220 ℃
Mold temperature range			80-100 ℃
water content			＜0.2 %
Pressure Range			80-100 MPa

Thermal performance	Test Condition	Test Method	Test Result
Heat distortion temperature		ISO 75-1/-2	165 ℃
Heat distortion temperature	Heat distortion temperature		ISO 75-1/-2	104 ℃
melting temperature		ISO 3146℃	178 ℃

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.