Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Melt volume flow rate | | | 10.0 cm³/10min |
| density | | | 1.20 g/cm³ |
| melt mass-flow rate | | | 10 g/10min |
| Shrinkage rate | | | 1.2to1.3 % |
| Water absorption rate | | | 0.75 % |
| Crystallinity | | | 60to70 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | | 57 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Temperature of Use | | | -30-120 °C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 70 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 无断裂 |
| Charpy Notched Impact Strength | | ISO 179/1eA | 3.4 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/1eA | 4.7 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | | 840to1200 MPa |
| tensile strength | Yield | | 15.0to20.0 MPa |
| Tensile strain | Break | | 8.0to15 % |
| bending strength | | | 18.0 MPa |
| bending strength | | | 16.0 MPa |
| bending strength | | | 4.7 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/A | 50.0 °C |
| vicat | | ISO 306/A120 | 134 °C |
| vicat | | ISO 306/B50 | 54.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.