Biodeg Polymers P209 Biomer
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | Biomer/P209 |
---|---|---|---|
Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 4.7 kJ/m² |
Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 无断裂 |
Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 3.4 kJ/m² |
Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 70 kJ/m² |
hardness | Test Condition | Test Method | Biomer/P209 |
---|---|---|---|
Shore hardness | 邵氏D | 57 |
Supplementary Information | Test Condition | Test Method | Biomer/P209 |
---|---|---|---|
Temperature of Use | -30-120 °C |
Mechanical properties | Test Condition | Test Method | Biomer/P209 |
---|---|---|---|
bending strength | 断裂弯曲应变 | 4.7 % | |
Tensile modulus | 840to1200 MPa | ||
bending strength | 3.5%应变 | 16.0 MPa | |
Tensile strain | 断裂 | 8.0to15 % | |
bending strength | -- | 18.0 MPa | |
tensile strength | 屈服 | 15.0to20.0 MPa |
physical property | Test Condition | Test Method | Biomer/P209 |
---|---|---|---|
melt mass-flow rate | 180°C/2.16kg | 10 g/10min | |
Shrinkage rate | 1.2to1.3 % | ||
density | 1.20 g/cm³ | ||
Crystallinity | 60to70 % | ||
Water absorption rate | 平衡,23°C,50%RH | 0.75 % | |
Melt volume flow rate | 180°C/2.16kg | 10.0 cm³/10min |
Thermal performance | Test Condition | Test Method | Biomer/P209 |
---|---|---|---|
vicat | -- | ISO 306/A120 | 134 °C |
Heat distortion temperature | 1.8MPa,未退火,HDT | ISO 75-2/A | 50.0 °C |
vicat | -- | ISO 306/B50 | 54.0 °C |