Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | g/10min | 17to22 |
| | ml/g | 80.0-95.0 |
| Melt volume flow rate | | cm³/10min | 0.05to0.07 |
| saturation | | % | 0.30-0.40 |
| Apparent density | | g/cm³ | 0.70-0.80 |
| balance | | % | 0.055-0.21 |
| lateral flow | | mm/mm | 188.0E-3-208.3E-3 |
| flow | | mm/mm | 86.4E-3-0.330 |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | | 110to120 |
| | | 110.34to251.72 Mpa |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Burning wire flammability index | | °C | 648to960 |
| Limiting Oxygen Index | | % | 21 |
| burning rate | | mm/min | 0.0to99.06 |
| Hot filament ignition temperature | | °C | 643to960 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| fracture | | | 97.24to160.0 Mpa |
| yield | | | 163.45to172.41 Mpa |
| yield | | | 87.59to175.17 Mpa |
| yield | | % | 1.0-3.0 |
| fracture | | | 50.0to140.69 Mpa |
| yield | | | 89.66to140.69 Mpa |
| fracture | | % | 1.5-3.2 |
| fracture | | % | 1.7-3.9 |
| yield | | % | 1.0-4.5 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | kJ/m² | 5.572to15.323 |
| Charpy Notched Impact Strength | | kJ/m² | 1.067to2.229 |
| Dart impact | | N.m | 469.91to626.55 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ohms | 1.0E+14-1.1E+15 |
| Volume resistivity | | ohms·cm | 1.0E+12-1.0E+16 |
| | | 3.76 |
| Compared to the Leakage Tracking Index (CTI) | | V | PLC 2 |
| Dissipation Factor | | | 8.0E-4-0.017 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| horizontal | | mm/mm/°C | 76.2E-5-101.6E-5 |
| RTI | | °C | 75to140 |
| RTI Elec | | °C | 75to140 |
| horizontal | | mm/mm/°C | 83.8E-5-152.4E-5 |
| RTI Imp | | °C | 75to125 |
| flow | | mm/mm/°C | 27.9E-5-50.8E-5 |
| flow | | mm/mm/°C | 30.5E-5-50.8E-5 |
| thermal conductivity | | W/m2k | 0.30to0.33 |
| melting temperature | | °C | 237to240 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.