PBT EPIMIX PBT CBR 20 NC 土耳其EPSAN
--
--
填料,玻璃珠,20%,填料按重量,
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | 土耳其EPSAN/EPIMIX PBT CBR 20 NC |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23℃ | kJ/m² | 5.572to15.323 |
| Charpy Notched Impact Strength | 23℃ | kJ/m² | 1.067to2.229 |
| Dart impact | 23℃ | N.m | 469.91to626.55 |
| hardness | Test Condition | Test Method | 土耳其EPSAN/EPIMIX PBT CBR 20 NC |
|---|---|---|---|
| 110.34to251.72 Mpa | |||
| Rockwell hardness | 23℃ | 110to120 |
| Mechanical properties | Test Condition | Test Method | 土耳其EPSAN/EPIMIX PBT CBR 20 NC |
|---|---|---|---|
| yield | % | 1.0-4.5 | |
| fracture | % | 1.7-3.9 | |
| yield | 89.66to140.69 Mpa | ||
| fracture | 50.0to140.69 Mpa |
| Electrical performance | Test Condition | Test Method | 土耳其EPSAN/EPIMIX PBT CBR 20 NC |
|---|---|---|---|
| 23℃ | 3.76 | ||
| Surface Resistivity | ohms | 1.0E+14-1.1E+15 | |
| Compared to the Leakage Tracking Index (CTI) | V | PLC 2 | |
| Volume resistivity | 23℃ | ohms·cm | 1.0E+12-1.0E+16 |
| Dissipation Factor | 23℃ | 8.0E-4-0.017 |
| flammability | Test Condition | Test Method | 土耳其EPSAN/EPIMIX PBT CBR 20 NC |
|---|---|---|---|
| Limiting Oxygen Index | % | 21 | |
| burning rate | mm/min | 0.0to99.06 | |
| Hot filament ignition temperature | °C | 643to960 | |
| Burning wire flammability index | °C | 648to960 |
| physical property | Test Condition | Test Method | 土耳其EPSAN/EPIMIX PBT CBR 20 NC |
|---|---|---|---|
| balance | % | 0.055-0.21 | |
| melt mass-flow rate | 265°C/2.16kg | g/10min | 17to22 |
| flow | mm/mm | 86.4E-3-0.330 | |
| 23℃ | ml/g | 80.0-95.0 | |
| Melt volume flow rate | 260°C/2.16kg | cm³/10min | 0.05to0.07 |
| saturation | % | 0.30-0.40 | |
| Apparent density | g/cm³ | 0.70-0.80 | |
| lateral flow | mm/mm | 188.0E-3-208.3E-3 |
| Thermal performance | Test Condition | Test Method | 土耳其EPSAN/EPIMIX PBT CBR 20 NC |
|---|---|---|---|
| RTI | °C | 75to140 | |
| flow | mm/mm/°C | 30.5E-5-50.8E-5 | |
| thermal conductivity | 23℃ | W/m2k | 0.30to0.33 |
| RTI Imp | °C | 75to125 | |
| RTI Elec | °C | 75to140 | |
| horizontal | mm/mm/°C | 83.8E-5-152.4E-5 | |
| melting temperature | °C | 237to240 |