PA66 TORZEN® G3500XHL BK02
9
- Properties:Glass fiber reinforced ma35% filler by weightHigh liquiditythermal stabilityGood demolding performanc
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ISO 294-4 | 0.90-1.1 % | |
| % | |||
| Water absorption rate | ISO 62 | 1.1 % | |
| Shrinkage rate | ISO 294-4 | 0.90-1.1 % | |
| ISO 294-4 | 0.25-0.35 % | ||
| Water absorption rate | ISO 62 | 1.1 % | |
| ISO 62 | 1.7 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 11500 Mpa | |
| tensile strength | ISO 527 | 210 Mpa | |
| Tensile strain | ISO 527 | 3.0 % | |
| Flexural modulus | ISO 178 | 10500 Mpa | |
| bending strength | ISO 178 | 320 Mpa | |
| Charpy Notched Impact Strength | ISO 179 | 10 kJ/m² | |
| Impact strength of simply supported beam without notch | ISO 179 | 12 kJ/m² | |
| Thermal performance | ISO 527-2/A | 250 °C | |
| melting temperature | ISO 11357-3 | 262 °C | |
| Tensile modulus | ISO 527-2 | 11500 Mpa | |
| tensile strength | ISO 527-2 | 210 Mpa | |
| Tensile strain | ISO 527-2 | 3.0 % | |
| Flexural modulus | ISO 178 | 10500 Mpa | |
| bending strength | ISO 178 | 320 Mpa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 262 °C | |
| Heat distortion temperature | ISO 75-2/B | 260 °C | |
| ISO 75-2/A | 250 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.