Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 G3500XHL BK02 INVISTA USA
TORZEN®
--
Glass fiber reinforced ma、35% filler by weight、High liquidity、thermal stability、Good demolding performanc
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | INVISTA USA/G3500XHL BK02 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 11500 Mpa | |
| Charpy Notched Impact Strength | -40℃ | ISO 179 | 10 kJ/m² |
| Tensile modulus | ISO 527-2 | 11500 Mpa | |
| Tensile strain | 断裂 | ISO 527 | 3.0 % |
| tensile strength | 断裂 | ISO 527 | 210 Mpa |
| bending strength | ISO 178 | 320 Mpa | |
| Flexural modulus | ISO 178 | 10500 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 3.0 % |
| Thermal performance | 1.8 MPa, 未退火 | ISO 527-2/A | 250 °C |
| tensile strength | 断裂 | ISO 527-2 | 210 Mpa |
| Impact strength of simply supported beam without notch | 23℃ | ISO 179 | 12 kJ/m² |
| melting temperature | ISO 11357-3 | 262 °C |
| physical property | Test Condition | Test Method | INVISTA USA/G3500XHL BK02 |
|---|---|---|---|
| Shrinkage rate | MD : 2.00 mm | % | |
| MD:2.00mm | ISO 294-4 | 0.25-0.35 % | |
| Water absorption rate | 23°C,24hr | ISO 62 | 1.1 % |
| 23℃, 24 hr | ISO 62 | 1.1 % | |
| Shrinkage rate | TD : 2.00 mm | ISO 294-4 | 0.90-1.1 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 1.7 % |
| Shrinkage rate | TD:2.00mm | ISO 294-4 | 0.90-1.1 % |
| Thermal performance | Test Condition | Test Method | INVISTA USA/G3500XHL BK02 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 262 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 260 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 250 °C |