PEI ULTEM™ EFL36-YWLTNAT
26
- Properties:Thermal stabilityUV resistance
- Usages:CastersHome appliance components
Technical Data Sheet
physical property | Test Condition | Test Method | Test Result |
---|---|---|---|
Shrinkage rate | ASTM D955 | 0.10-0.30 % | |
ASTM D955 | 0.40-0.60 % | ||
ISO 294-4 | 0.21-0.24 % | ||
Water absorption rate | ASTM D570 | 0.15 % | |
ISO 62 | 0.22 % |
Mechanical properties | Test Condition | Test Method | Test Result |
---|---|---|---|
Tensile modulus | ASTM D638 | 12700 Mpa | |
ISO 527-2/1 | 11200 Mpa | ||
tensile strength | ASTM D638 | 176 Mpa | |
ISO 527-2 | 168 Mpa | ||
elongation | ASTM D638 | 2.0 % | |
Tensile strain | ISO 527-2 | 2.0 % | |
Flexural modulus | ASTM D790 | 11300 Mpa | |
ISO 178 | 11400 Mpa | ||
bending strength | ASTM D790 | 253 Mpa | |
ISO 178 | 249 Mpa | ||
coefficient of friction | ASTM D3702Modified | 0.46 | |
ASTM D3702Modified | 0.43 | ||
Wear factor | ASTM D3702Modified | 35.0 10^-10in^5-min/ft-lb-hr |
Impact resistance | Test Condition | Test Method | Test Result |
---|---|---|---|
Impact strength of cantilever beam gap | ISO 180/1A | 13 kJ/m² | |
Suspended wall beam without notch impact strength | ISO 180/1U | 47 kJ/m² | |
Dart impact | ASTM D3763 | 10.3 J | |
Multi axis Instrumented Impact Energy | ISO 6603-2 | 3.65 J |
Thermal performance | Test Condition | Test Method | Test Result |
---|---|---|---|
Heat distortion temperature | ASTM D648 | 202 °C | |
ISO 75-2/Af | 204 °C | ||
Linear coefficient of thermal expansion | ASTME831 | 4E-05 cm/cm/°C | |
ISO 11359-2 | 4E-05 cm/cm/°C | ||
ASTME831 | 2.7E-05 cm/cm/°C | ||
ISO 11359-2 | 2.8E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.