PEI EFL36-YWLTNAT SABIC INNOVATIVE US
ULTEM™ 
Casters、Home appliance components
Thermal stability、UV resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC INNOVATIVE US/EFL36-YWLTNAT
Suspended wall beam without notch impact strength23°CISO 180/1U47 kJ/m²
Multi axis Instrumented Impact EnergyISO 6603-23.65 J
Impact strength of cantilever beam gap23°CISO 180/1A13 kJ/m²
Dart impact23°C,EnergyatPeakLoadASTM D376310.3 J
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/EFL36-YWLTNAT
Tensile modulusISO 527-2/111200 Mpa
bending strengthASTM D790253 Mpa
tensile strength 断裂ASTM D638176 Mpa
断裂ISO 527-2168 Mpa
Wear factorWasherASTM D3702Modified35.0 10^-10in^5-min/ft-lb-hr
Flexural modulusASTM D79011300 Mpa
Tensile modulusASTM D63812700 Mpa
elongation断裂ASTM D6382.0 %
bending strengthISO 178249 Mpa
coefficient of frictionStaticASTM D3702Modified0.43
Tensile strain断裂ISO 527-22.0 %
Flexural modulusISO 17811400 Mpa
coefficient of frictionDynamicASTM D3702Modified0.46
physical property Test ConditionTest MethodSABIC INNOVATIVE US/EFL36-YWLTNAT
Shrinkage rateMD：24小时ASTM D9550.10-0.30 %
Water absorption rate24hr,50%RHASTM D5700.15 %
平衡,23°C,50%RHISO 620.22 %
Shrinkage rateTD：24hrASTM D9550.40-0.60 %
MD：24小时ISO 294-40.21-0.24 %
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE US/EFL36-YWLTNAT
Linear coefficient of thermal expansionTD：-40到40°CASTME8312.7E-05 cm/cm/°C
TD：-40到40°CISO 11359-22.8E-05 cm/cm/°C
MD：-40到40°CASTME8314E-05 cm/cm/°C
MD：-40到40°CISO 11359-24E-05 cm/cm/°C
Heat distortion temperature1.8MPa,未退火,64.0mm跨距，HDTISO 75-2/Af204 °C
1.8MPa,未退火,3.20mm，HDTASTM D648202 °C