PA610 LNP™ THERMOCOMP™ QC006 compound
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792 | 1.20 g/cm³ | |
| ASTM D792 | 1.24 g/cm³ | ||
| Shrinkage rate | ASTM D955 | 0.10to0.30 % | |
| ASTM D955 | 0.80to1.0 % | ||
| Water absorption rate | ASTM D570 | 0.20 % | |
| ISO 62 | 0.30 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| elongation | ASTM D638 | 3.0 % | |
| Break | ISO 527-2/5 | 2.2 % | |
| Flexural modulus | ASTM D790 | 16100 MPa | |
| ISO 178 | 18800 MPa | ||
| bending strength | ISO 178 | 349 MPa | |
| ASTM D790 | 326 MPa | ||
| ASTM D790 | 325 MPa | ||
| Tensile modulus | ISO 527-2/1 | 23000 MPa | |
| tensile strength | ASTM D638 | 214 MPa | |
| Break | ISO 527-2/5 | 243 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256 | 100 J/m | |
| ISO 180/1A | 12 kJ/m² | ||
| Suspended wall beam without notch impact strength | ASTM D4812 | 920 J/m | |
| ISO 180/1U | 59 kJ/m² | ||
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 4.00 J |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 220 °C | |
| ISO 75-2/Bf | 221 °C | ||
| ASTM D648 | 211 °C | ||
| ISO 75-2/Af | 213 °C | ||
| Linear coefficient of thermal expansion | ASTM D696 | 1.2E-05 cm/cm/°C | |
| ASTM D696 | 5.5E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.