PA610 LNP™ THERMOCOMP™ QC006 compound SABIC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC/LNP™ THERMOCOMP™ QC006 compound
Impact strength of cantilever beam gap23°CASTM D256100 J/m
Suspended wall beam without notch impact strength23°CASTM D4812920 J/m
23°C5ISO 180/1U59 kJ/m²
Multi axis Instrumented Impact EnergyISO 6603-24.00 J
Impact strength of cantilever beam gap23°C5ISO 180/1A12 kJ/m²
Mechanical propertiesTest ConditionTest MethodSABIC/LNP™ THERMOCOMP™ QC006 compound
Flexural modulus50.0mm跨距3ASTM D79016100 MPa
elongation断裂2ASTM D6383.0 %
tensile strength 断裂ISO 527-2/5243 MPa
bending strength断裂,50.0mm跨距3ASTM D790325 MPa
Flexural modulus--4ISO 17818800 MPa
bending strength屈服,50.0mm跨距3ASTM D790326 MPa
--ISO 178349 MPa
Tensile modulusISO 527-2/123000 MPa
elongation断裂ISO 527-2/52.2 %
tensile strength 断裂2ASTM D638214 MPa
physical property Test ConditionTest MethodSABIC/LNP™ THERMOCOMP™ QC006 compound
Water absorption rate24hr,50%RHASTM D5700.20 %
Shrinkage rateTD:24小时ASTM D9550.80to1.0 %
Water absorption rate平衡,23°C,50%RHISO 620.30 %
density--ASTM D7921.24 g/cm³
Shrinkage rateMD:24小时ASTM D9550.10to0.30 %
Thermal performanceTest ConditionTest MethodSABIC/LNP™ THERMOCOMP™ QC006 compound
Linear coefficient of thermal expansionMD:-30到30°CASTM D6961.2E-05 cm/cm/°C
Heat distortion temperature0.45MPa,未退火,3.20mm，HDTASTM D648220 °C
0.45MPa,未退火,64.0mm跨距6，HDTISO 75-2/Bf221 °C
1.8MPa,未退火,64.0mm跨距6，HDTISO 75-2/Af213 °C
Linear coefficient of thermal expansionTD:-30到30°CASTM D6965.5E-05 cm/cm/°C
Heat distortion temperature1.8MPa,未退火,3.20mm，HDTASTM D648211 °C