HDPE SP 4808
0
- Usages:Pipeline system
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTMD1505 | 0.949 g/cm³ | |
| melt mass-flow rate | ASTMD1238 | 0.060 g/10min | |
| ASTMD1238 | 9.0 g/10min | ||
| ASTMD1238 | 0.25 g/10min | ||
| Resistance to environmental stress cracking | ASTMD1693 | >1000 hr | |
| >100000000 mPa·s |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hydrostatic Resistance | ISO1167 | >4.2 day | |
| ISO1167 | >41.7 day | ||
| ISO1167 | >6.9 day | ||
| LongitudinalReversion | ISO2505-1,-2 | 0.63 % | |
| RapidCrackPropagation-S | ISO13477 | >1.20 MPa |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | Yield | ASTMD638 | 30.0 MPa |
| Break | ASTMD638 | 50.0 MPa | |
| elongation | Break | ASTMD638 | >700 % |
| Flexural modulus | ASTMD790 | 1300 MPa | |
| SlowCrackGrowthResistance-NotchTest | >1058 hr |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile impact strength | ASTMD1822 | 550 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| brittle temperature | ASTMD746 | <-70.0 °C | |
| ASTMD3895 | >80 min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.