HDPE SP 4808 Chandra Asri Petrochemical
--
Pipeline system
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Chandra Asri Petrochemical/ SP 4808 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D1822 | 550 kJ/m² |
| Supplementary Information | Test Condition | Test Method | Chandra Asri Petrochemical/ SP 4808 |
|---|---|---|---|
| LongitudinalReversion | ISO 2505-1 | 0.63 % | |
| RapidCrackPropagation-S | 0°C | ISO 13477 | >1.20 MPa |
| Hydrostatic Resistance | 5.5MPa:80°C | ISO 1167 | >6.9 day |
| 5.0MPa:80°C | ISO 1167 | >41.7 day | |
| 12.4MPa:20°C | ISO 1167 | >4.2 day |
| Mechanical properties | Test Condition | Test Method | Chandra Asri Petrochemical/ SP 4808 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | >700 % |
| tensile strength | 断裂 | ASTM D638 | 50.0 MPa |
| Flexural modulus | ASTM D790 | 1300 MPa | |
| tensile strength | 屈服 | ASTM D638 | 30.0 MPa |
| SlowCrackGrowthResistance-NotchTest | 80°C | >1058 hr |
| physical property | Test Condition | Test Method | Chandra Asri Petrochemical/ SP 4808 |
|---|---|---|---|
| density | ASTM D1505 | 0.949 g/cm³ | |
| melt mass-flow rate | 190°C/21.6kg | ASTM D1238 | 9.0 g/10min |
| Viscosity | 190°C | >100000000 mPa·s | |
| Environmental stress cracking resistance | 10%Igepal,F50 | ASTM D1693 | >1000 hr |
| melt mass-flow rate | 190°C/5.0kg | ASTM D1238 | 0.25 g/10min |
| 190°C/2.16kg | ASTM D1238 | 0.060 g/10min |
| Thermal performance | Test Condition | Test Method | Chandra Asri Petrochemical/ SP 4808 |
|---|---|---|---|
| brittle temperature | ASTM D746 | <-70.0 °C | |
| Oxygen induction time | 200°C | ASTM D3895 | >80 min |