ABS TAROBLEND 60 X0

Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
Water absorption rate	Saturation	ASTMD570	0.70 %
Water absorption rate	Water absorption rate		ISO62	0.70 %
density		ASTMD792,ISO1183	1.19到1.21 g/cm³
Shrinkage rate		ASTMD955	0.40到0.60 %
Shrinkage rate	Shrinkage rate		ASTMD955	0.40到0.60 %
Water absorption rate		ASTMD570,ISO62	0.30 %

flammability	Test Method	Test Result
UL flame retardant rating	UL94	V-0
Hot filament ignition temperature	IEC60695-2-13	960 °C
Limiting Oxygen Index	ASTMD2863	32 %

Mechanical properties	Test Condition	Test Method	Test Result
Bending stress		ISO178	90.0 MPa
Bending stress	Bending stress	Yield	ASTMD790	90.0 MPa
tensile strength	Yield	ASTMD638,ISO527-2	65.0 MPa
elongation	Break	ASTMD638,ISO527-2	40 %
Flexural modulus		ASTMD790,ISO178	2550 MPa
Tensile modulus		ASTMD638,ISO527-2	2750 MPa

Impact resistance	Test Method	Test Result
Charpy Notched Impact Strength	ISO179,ASTMD256	22 kJ/m²
Impact strength of simply supported beam without notch	ISO179,ASTMD256	无断裂
Impact strength of cantilever beam gap	ASTMD256,ISO180	450 J/m

Thermal performance	Test Method	Test Result
vicat	ISO306/A50,ASTMD15255	122 °C
BallPressure Test	VDE0470	通过
	ASTMD696	7E-05 cm/cm/°C
		ASTMD648,ISO75-2/A	88.0 °C
Continuous use temperature	UL746B	60.0 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.