ABS TAROBLEND 60 X0 Taro Plast S.p.A.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Taro Plast S.p.A./TAROBLEND 60 X0 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 22 kJ/m² |
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTMD256 | 450 J/m |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 无断裂 |
| Mechanical properties | Test Condition | Test Method | Taro Plast S.p.A./TAROBLEND 60 X0 |
|---|---|---|---|
| Flexural modulus | ASTMD790 | 2550 MPa | |
| elongation | 断裂 | ASTMD638 | 40 % |
| bending strength | 屈服 | ASTM D790 | 90.0 MPa |
| Tensile modulus | ASTMD638 | 2750 MPa | |
| tensile strength | 屈服 | ASTMD638 | 65.0 MPa |
| bending strength | --3 | ISO 178 | 90.0 MPa |
| flammability | Test Condition | Test Method | Taro Plast S.p.A./TAROBLEND 60 X0 |
|---|---|---|---|
| Hot filament ignition temperature | 2.0mm | IEC 60695-2-13 | 960 °C |
| UL flame retardant rating | 1.7mm | UL 94 | V-0 |
| Limiting Oxygen Index | ASTM D2863 | 32 % |
| physical property | Test Condition | Test Method | Taro Plast S.p.A./TAROBLEND 60 X0 |
|---|---|---|---|
| Water absorption rate | 饱和 | ASTM D570 | 0.70 % |
| Shrinkage rate | MD | ASTM D955 | 0.40to0.60 % |
| density | ASTMD792 | 1.19to1.21 g/cm³ | |
| Water absorption rate | 23°C,24hr | ASTMD570 | 0.30 % |
| 饱和,23°C | ISO 62 | 0.70 % | |
| Shrinkage rate | TD | ASTM D955 | 0.40to0.60 % |
| Thermal performance | Test Condition | Test Method | Taro Plast S.p.A./TAROBLEND 60 X0 |
|---|---|---|---|
| vicat | ISO 306/A50 | 122 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTMD648 | 88.0 °C |
| Linear coefficient of thermal expansion | MD：-30到30°C | ASTM D696 | 7E-05 cm/cm/°C |
| ball-indentation hardness | 75°C | VDE0470 | 通过 |
| Continuous use temperature | UL 746B | 60.0 °C |