physical property | Test Condition | Test Method | Test Result |
---|
Shrinkage rate | | ISO 294-4 | 0.80 % |
Shrinkage rate | | ISO 294-4 | 0.30 % |
Water absorption rate | | ISO 62 | 1.9 % |
Water absorption rate | | ISO 62 | 5.0 % |
flammability | Test Condition | Test Method | Test Result |
---|
UL flame retardant rating | | UL 94 | V-0 |
UL flame retardant rating | | UL 94 | V-0 |
UL flame retardant rating | | UL 94 | V-0 |
UL flame retardant rating | | UL 94 | V-0 |
Burning wire flammability index | | IEC 60695-2-12 | 960 °C |
Burning wire flammability index | | IEC 60695-2-12 | 960 °C |
Hot filament ignition temperature | | IEC 60695-2-13 | 775 °C |
Hot filament ignition temperature | | IEC 60695-2-13 | 800 °C |
Limiting Oxygen Index | | ISO 4589-2 | 30 % |
Mechanical properties | Test Condition | Test Method | Test Result |
---|
Tensile modulus | | ISO 527-2 | 8000 Mpa |
tensile strength | | ISO 527-2 | 170 Mpa |
Tensile strain | | ISO 527-2 | 4.5 % |
Impact resistance | Test Condition | Test Method | Test Result |
---|
Impact strength of simply supported beam without notch | | ISO 179/1eU | 无断裂 |
Impact strength of simply supported beam without notch | | ISO 179/1eU | 无断裂 |
Electrical performance | Test Condition | Test Method | Test Result |
---|
Volume resistivity | | IEC 60093 | 1E+15 ohms·cm |
dielectric strength | | IEC 60243-1 | 18 KV/mm |
Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
needle flame test | | IEC 60695-11-5 | 通过 |
needle flame test | | IEC 60695-11-5 | 通过 |
Surface Resistivity | | IEC 60093 | 1E+13 ohms |
Thermal performance | Test Condition | Test Method | Test Result |
---|
Heat distortion temperature | | ISO 75-2/B | 220 °C |
Heat distortion temperature | | ISO 75-2/A | 210 °C |
Continuous use temperature | | IEC 60216 | 110 °C |
ball-indentation hardness | | IEC 60695-10-2 | 通过 |
ball-indentation hardness | | IEC 60695-10-2 | 通过 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.