Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ASTMD995 | 1.0 % |
| Water absorption rate | | ASTMD570 | 0.75 % |
| density | | ASTMD792 | 1.17 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTMD785 | 105 R |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTMD638 | 72.0 MPa |
| elongation at break | | ASTMD638 | 50 % |
| bending strength | | ASTMD790 | 103 MPa |
| Flexural modulus | | ASTMD790 | 2600 MPa |
| Impact strength of cantilever beam gap | | ASTMD256 | 78.0 J/m |
| Flame retardant performance | Test Condition | Test Method | Test Result |
|---|
| fire rating | | UL-94 | 3.00mm HB |
| fire rating | | UL-94 | 0.81mm HB |
| fire rating | | UL-94 | 1.50mm HB |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| | ASTMD257 | 1E+10 Ω.cm |
| Dielectric Strength | | ASTMD149 | 22 KV/mm |
| dielectric constant | | ASTMD150 | 3.6 1MHz |
| Dissipation Factor | | ASTMD150 | 0.040 |
| Dissipation Factor | | ASTMD3638 | >=600 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ASTMD648 | 150 °C |
| | ASTMD696 | 7.7E-05 cm/cm／°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare