Polyarylate U-polymer AX-1500 UNITIKA JAPAN
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | UNITIKA JAPAN/U-polymer AX-1500 |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | 105 R |
| Mechanical properties | Test Condition | Test Method | UNITIKA JAPAN/U-polymer AX-1500 |
|---|---|---|---|
| bending strength | 23°C | ASTM D790 | 103 MPa |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 78.0 J/m |
| tensile strength | 23°C | ASTM D638 | 72.0 MPa |
| Flexural modulus | 23°C | ASTM D790 | 2600 MPa |
| elongation at break | 23°C | ASTM D638 | 50 % |
| Electrical performance | Test Condition | Test Method | UNITIKA JAPAN/U-polymer AX-1500 |
|---|---|---|---|
| Dissipation Factor | ASTM D150 | 0.040 | |
| Volume resistivity | ASTM D257 | 1E+10 Ω.cm | |
| dielectric strength | ASTM D149 | 22 KV/mm | |
| dielectric constant | ASTM D150 | 3.6 1MHz | |
| Dissipation Factor | 相对漏电起痕指数 | ASTM D3638 | >=600 V |
| Flame retardant performance | Test Condition | Test Method | UNITIKA JAPAN/U-polymer AX-1500 |
|---|---|---|---|
| UL flame retardant rating | UL -94 | HB 1.50mm | |
| UL -94 | HB 3.00mm | ||
| UL -94 | HB 0.81mm |
| physical property | Test Condition | Test Method | UNITIKA JAPAN/U-polymer AX-1500 |
|---|---|---|---|
| Shrinkage rate | MD3.00mm | ASTM D995 | 1.0 % |
| Water absorption rate | (23°C,24hr) | ASTM D570 | 0.75 % |
| density | ASTM D792 | 1.17 g/cm³ |
| Thermal performance | Test Condition | Test Method | UNITIKA JAPAN/U-polymer AX-1500 |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD | ASTM D696 | 7.7E-05 cm/cm／°C |
| Heat distortion temperature | 1.80MPa未退火，HDT | ASTM D648 | 150 °C |