Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ASTMD955 | 0.30to1.4 % |
| Water absorption rate | | ASTMD570 | 0.070 % |
| density | | ASTMD792 | 1.52 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTMD785 | 118 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| elongation | | ASTMD638 | 2.2 % |
| Flexural modulus | | ASTMD790 | 8480 Mpa |
| compressive strength | | ASTMD695 | 157 Mpa |
| Tensile modulus | | ASTMD638 | 11900 Mpa |
| tensile strength | | ASTMD638 | 125 Mpa |
| bending strength | | ASTMD790 | 189 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256 | 91 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | ASTMD149 | 29 KV/mm |
| dielectric constant | | ASTMD150 | 2.20 |
| Volume resistivity | | ASTMD257 | 1E+16 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| melting temperature | | DSC | 224 °C |
| | ASTMD696 | 3.1E-05 cm/cm/°C |
| | ASTMD648 | 208 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.