PC IUPILON™ H-2000R MITSUBISHI THAILAND
746
- Properties:High mobility
- Usages:Automotive sectorMedical packagingElectronic fieldElectrical field
- Certificates:ULUL
Compare
View PricesTechnical Data Sheet
| 物理性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 熔体质量流动速率 | 300°C/1.2kg | ISO1133 | 22 g/10min |
| 熔体体积流动速率 | 300°C/1.2kg | ISO1133 | 20.0 cm3/10min |
| 收缩率 | TD:3.20mm | 0.50to0.70 % | |
| MD:3.20mm | 0.50to0.70 % | ||
| 吸水率(饱和,23°C) | 0.24 % |
| 热性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 热变形温度 | 0.45MPa,未退火 | ISO75-2/B | 138 °C |
| 1.8MPa,未退火 | ISO75-2/A | 124 °C | |
| 线性热膨胀系数 | MD | ISO11359-2 | 6.5E-05 cm/cm/°C |
| TD | ISO11359-2 | 6.6E-05 cm/cm/°C |
| 机械性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 弯曲模量 | ISO178 | 2300 Mpa | |
| 弯曲应力 | ISO178 | 93.0 Mpa | |
| 拉伸模量 | ISO527-2 | 2400 Mpa | |
| 拉伸应力 | 屈服 | ISO527-2 | 62.0 Mpa |
| 拉伸应变 | 屈服 | ISO527-2 | 6.6 % |
| 标称拉伸断裂应变 | ISO527-2 | 120 % |
| 电气性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 表面电阻率 | IEC60093 | 6E+15 ohms | |
| 体积电阻率 | IEC60093 | 3E+16 ohms·cm | |
| 介电强度 | 1.00mm | IEC60243-1 | 31 KV/mm |
| 3.00mm | IEC60243-1 | 18 KV/mm | |
| 相对电容率 | 100Hz | IEC60250 | 3.10 |
| 1MHz | IEC60250 | 3.10 | |
| 耗散因数 | 100Hz | IEC60250 | 6E-04 |
| 1MHz | IEC60250 | 9E-03 | |
| 相比耐漏电起痕指数(CTI) | CTI | UL746 | PLC 2 |
| 冲击性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 简支梁无缺口冲击强度 | 23°C | ISO179 | NoBreak |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.