Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC H-2000R MITSUBISHI THAILAND
IUPILON™ 
Automotive sector、Medical packaging、Electronic field、Electrical field
High mobility
UL
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Thermal PropertiesTest ConditionTest MethodMITSUBISHI THAILAND/H-2000R
Linear thermal expansion coefficientMDISO11359-26.5E-05 cm/cm/°C
Heat Deflection Temperature0.45MPa,未退火ISO75-2/B138 °C
1.8MPa,未退火ISO75-2/A124 °C
Linear thermal expansion coefficientTDISO11359-26.6E-05 cm/cm/°C
Mechanical PropertiesTest ConditionTest MethodMITSUBISHI THAILAND/H-2000R
Flexural ModulusISO1782300 Mpa
Tensile Strain屈服ISO527-26.6 %
Tensile Stress屈服ISO527-262.0 Mpa
Nominal Tensile Strain at BreakISO527-2120 %
Flexural StressISO17893.0 Mpa
Tensile ModulusISO527-22400 Mpa
PhysicalTest ConditionTest MethodMITSUBISHI THAILAND/H-2000R
Melt Mass-Flow Rate300°C/1.2kgISO113322 g/10min
Modeling Shrinkage吸水率(饱和,23°C)0.24 %
TD:3.20mm0.50to0.70 %
Melt Volume flow Rate300°C/1.2kgISO113320.0 cm3/10min
Modeling ShrinkageMD:3.20mm0.50to0.70 %
Impact PropertiesTest ConditionTest MethodMITSUBISHI THAILAND/H-2000R
Charpy Unnotched Impact Strength23°CISO179NoBreak
Electrical PropertiesTest ConditionTest MethodMITSUBISHI THAILAND/H-2000R
Volume ResistivityIEC600933E+16 ohms·cm
Dielectric Strength3.00mmIEC60243-118 KV/mm
Surface ResistivityIEC600936E+15 ohms
Relative Permittivity1MHzIEC602503.10
100HzIEC602503.10
Dielectric Strength1.00mmIEC60243-131 KV/mm
Dissipation Factor?1MHzIEC602509E-03
100HzIEC602506E-04
Comparative Tracking IndexCTIUL746PLC 2