POM/PTFE LNP™ LUBRICOMP™ KFX-1002
37
- Properties:High temperature resistanLow temperature resistancFiller: Glass fiber reinf10% filler by weight
- Usages:Electronic and electrical componentsLaptop case
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ASTMD955 | 1.2 % | |
| ASTMD955 | 1.3 % | ||
| ISO294-4 | 1.3 % | ||
| ISO294-4 | 1.2 % | ||
| Water absorption rate | ASTMD570 | 0.19 % | |
| ISO62 | 0.35 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTMD638 | 4760 Mpa | |
| ISO527-2/1 | 5400 Mpa | ||
| tensile strength | ASTMD638 | 84.5 Mpa | |
| Tensile stress | ISO527-2 | 86.4 Mpa | |
| elongation | ASTMD638 | 3.2 % | |
| Tensile strain | ISO527-2 | 3.4 % | |
| Flexural modulus | ASTMD790 | 4620 Mpa | |
| ISO178 | 5400 Mpa | ||
| bending strength | ASTMD790 | 129 Mpa | |
| Bending stress | ISO178 | 137 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Suspended wall beam gap impact strength 3 | ISO180/1A | 5.3 kJ/m² | |
| UnnotchedIzodImpactStrength3 | ISO180/1U | 33 kJ/m² | |
| Multi axis Instrumented Impact Energy | ISO6603-2 | 1.45 J |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ASTMD648 | 164 °C | ||
| ASTMD648 | 162 °C | ||
| Hot deformation temperature 4 | ISO75-2/Af | 161 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.