POM/PTFE KFX-1002 SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Electronic and electrical、Laptop case
High temperature resistan、Low temperature resistanc、Filler: Glass fiber reinf、10% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/KFX-1002 |
|---|---|---|---|
| Suspended wall beam gap impact strength 3 | 23°C | ISO180/1A | 5.3 kJ/m² |
| UnnotchedIzodImpactStrength3 | 23°C | ISO180/1U | 33 kJ/m² |
| Multi axis Instrumented Impact Energy | ISO6603-2 | 1.45 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/KFX-1002 |
|---|---|---|---|
| Tensile stress | 断裂 | ISO527-2 | 86.4 Mpa |
| Tensile modulus | ISO527-2/1 | 5400 Mpa | |
| elongation | 断裂 | ASTMD638 | 3.2 % |
| Flexural modulus | ASTMD790 | 4620 Mpa | |
| Bending stress | ISO178 | 137 Mpa | |
| tensile strength | 断裂 | ASTMD638 | 84.5 Mpa |
| Tensile modulus | ASTMD638 | 4760 Mpa | |
| Flexural modulus | ISO178 | 5400 Mpa | |
| bending strength | ASTMD790 | 129 Mpa | |
| Tensile strain | 断裂 | ISO527-2 | 3.4 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/KFX-1002 |
|---|---|---|---|
| Shrinkage rate | TD：24hr | ASTMD955 | 1.3 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO62 | 0.35 % |
| Shrinkage rate | MD:24小时 | ISO294-4 | 1.2 % |
| TD:24小时 | ISO294-4 | 1.3 % | |
| Water absorption rate | 24hr,50%RH | ASTMD570 | 0.19 % |
| Shrinkage rate | MD：24小时 | ASTMD955 | 1.2 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/KFX-1002 |
|---|---|---|---|
| 1.8MPa,未退火,3.20mm | ASTMD648 | 162 °C | |
| 0.45MPa,未退火,3.20mm | ASTMD648 | 164 °C | |
| Hot deformation temperature 4 | 1.8MPa,未退火,64.0mm跨距 | ISO75-2/Af | 161 °C |