ABS Lustran® 308 NR
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.40to0.60 % | |
| melt mass-flow rate | ASTM D1238 | 7.0 g/10min | |
| ASTM D1238 | 21 g/10min | ||
| density | ASTM D792 | 1.06 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | R-Scale | ASTM D785 | 105 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256 | 170 J/m |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| bending strength | ASTM D790 | 72.4 MPa | |
| Flexural modulus | ASTM D790 | 2450 MPa | |
| tensile strength | ASTM D638 | 36.2 MPa | |
| Tensile modulus | ASTM D638 | 2210 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 75.6 °C | |
| ASTM D648 | 100 °C | ||
| ASTM D648 | 88.9 °C | ||
| Linear coefficient of thermal expansion | ASTM D696 | 9E-05 cm/cm/°C | |
| vicat | ASTM D15252 | 106 °C | |
| Heat distortion temperature | ASTM D648 | 95.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.