ABS Lustran® 308 NR INEOS Barex
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | INEOS Barex/Lustran® 308 NR |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 170 J/m |
| hardness | Test Condition | Test Method | INEOS Barex/Lustran® 308 NR |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 105 |
| Mechanical properties | Test Condition | Test Method | INEOS Barex/Lustran® 308 NR |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2210 MPa | |
| Flexural modulus | ASTM D790 | 2450 MPa | |
| bending strength | ASTM D790 | 72.4 MPa | |
| tensile strength | 屈服,23°C | ASTM D638 | 36.2 MPa |
| physical property | Test Condition | Test Method | INEOS Barex/Lustran® 308 NR |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.40to0.60 % |
| melt mass-flow rate | 230°C/3.8kg | ASTM D1238 | 7.0 g/10min |
| density | ASTM D792 | 1.06 g/cm³ | |
| melt mass-flow rate | 220°C/10.0kg | ASTM D1238 | 21 g/10min |
| Thermal performance | Test Condition | Test Method | INEOS Barex/Lustran® 308 NR |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 75.6 °C |
| 0.45MPa,未退火，HDT | ASTM D648 | 88.9 °C | |
| 1.8MPa,退火，HDT | ASTM D648 | 95.0 °C | |
| vicat | ASTM D15252 | 106 °C | |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 9E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,退火，HDT | ASTM D648 | 100 °C |