PPA/F/PTFE LNP™ LUBRICOMP™ UFL-36S BK1A956
27
- Properties:Thermal stabilitywear resistant
- Usages:Car hoodPlastic bagbearingElectrical appliances
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Longitudinal shrinkage rate (Flow) | ISO 294 | 0.17 % | |
| ASTM D 955 | 0.2 % | ||
| Shrinkage rate (Across Flow) | ASTM D 955 | 0.8 % | |
| ISO 294 | 0.82 % | ||
| Moisture absorption rate | ASTM D 570 | 0.33 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile strength fracture (brk) | ASTM D638 | 196 Mpa | |
| ISO 527 | 196 Mpa | ||
| ASTM D638 | 2.5 % | ||
| ISO 527 | 2.5 % | ||
| bending strength | ASTM D790 | 280 Mpa | |
| ISO 178 | 280 Mpa | ||
| Flexural modulus | ASTM D790 | 10820 Mpa | |
| ISO 178 | 11230 Mpa | ||
| ASTM D 3702 | 0.46 / | ||
| ASTM D 3702 | 0.49 / | ||
| Wear factor | ASTM D 3702 | 6 E-10 in5·min/ft·lb·hr |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ISO 180/1A | 12 kJ/m² | ||
| ASTM D256 | 117 J/m | ||
| ISO 180/1U | 70 kJ/m² | ||
| ASTM D4812 | 1014 J/m | ||
| Instrumented dart impact energy peak at 23 ℃ (73 ℉) | ASTM D3763 | 7 J | |
| Multi axis impact | ISO 6603 | 3 J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.