PPA/F/PTFE UFL-36S BK1A956 SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Car hood、Plastic bag、bearing、Electrical appliances
Thermal stability、wear resistant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/UFL-36S BK1A956 |
|---|---|---|---|
| Multi axis impact | / | ISO 6603 | 3 J |
| Impact strength of cantilever beam gap | 23℃ (73℉) | ISO 180/1A | 12 kJ/m² |
| 23℃ (73℉)80*10*4 | ASTM D256 | 117 J/m | |
| Suspended wall beam without notch impact strength | 23℃ (73℉) | ASTM D4812 | 1014 J/m |
| Instrumented dart impact energy peak at 23 ℃ (73 ℉) | / | ASTM D3763 | 7 J |
| Suspended wall beam without notch impact strength | 23℃ (73℉)80*10*4 | ISO 180/1U | 70 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/UFL-36S BK1A956 |
|---|---|---|---|
| tensile strength | /，断裂 | ASTM D638 | 196 Mpa |
| Wear factor | Wear Fa | ASTM D 3702 | 6 E-10 in5·min/ft·lb·hr |
| elongation at break | / | ASTM D638 | 2.5 % |
| bending strength | / | ASTM D790 | 280 Mpa |
| coefficient of friction | Dynamic | ASTM D 3702 | 0.46 / |
| tensile strength | /，断裂 | ISO 527 | 196 Mpa |
| Flexural modulus | / | ISO 178 | 11230 Mpa |
| bending strength | / | ISO 178 | 280 Mpa |
| Flexural modulus | / | ASTM D790 | 10820 Mpa |
| elongation at break | / | ISO 527 | 2.5 % |
| coefficient of friction | Static C | ASTM D 3702 | 0.49 / |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/UFL-36S BK1A956 |
|---|---|---|---|
| Shrinkage rate | flow, 24 h | ISO 294 | 0.17 % |
| xflow, 24，Across Flow | ASTM D 955 | 0.8 % | |
| flow, 24 h | ASTM D 955 | 0.2 % | |
| Water absorption rate | 50% RH, | ASTM D 570 | 0.33 % |
| Shrinkage rate | xflow, 24，Across Flow | ISO 294 | 0.82 % |