Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | 内部方法 | 0.50to0.70 % |
| Water absorption rate | | ISO62 | 0.10 % |
| density | | ISO1183 | 1.08 g/cm³ |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-2 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile stress | | ISO527-2 | 44.0 MPa |
| Nominal tensile fracture strain | | ISO527-2 | 21 % |
| Flexural modulus | | ISO178 | 2270 MPa |
| Bending stress | | ISO178 | 72.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179 | 15 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | 1E+16 ohms |
| Volume resistivity | | IEC60093 | 1E+16 ohms·cm |
| dielectric strength | | IEC60243-1 | 29 kV/mm |
| dielectric constant | | IEC60250 | 2.90 |
| dielectric constant | | IEC60250 | 2.90 |
| Dissipation Factor | | IEC60250 | 3E-03 |
| Dissipation Factor | | IEC60250 | 4E-03 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ASTMD648 | 100 °C |
| | ISO75-2/A | 94.0 °C |
| | ISO11359-2 | 7.5E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.