PPO(PPE)+PS XYRON™ 340W ASAHI JAPAN
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodASAHI JAPAN/XYRON™ 340W
Charpy Notched Impact Strength23°CISO 17915 kJ/m²
Electrical performanceTest ConditionTest MethodASAHI JAPAN/XYRON™ 340W
dielectric constant100HzIEC 602502.90
Dissipation Factor100HzIEC 602503E-03
Volume resistivity23°CIEC 600931E+16 ohms·cm
dielectric strength2.00mmIEC 60243-129 kV/mm
dielectric constant1MHzIEC 602502.90
Surface ResistivityIEC 600931E+16 ohms
Dissipation Factor1MHzIEC 602504E-03
Mechanical propertiesTest ConditionTest MethodASAHI JAPAN/XYRON™ 340W
Flexural modulus23°CISO 1782270 MPa
tensile strength 屈服,23°CISO 527-244.0 MPa
Nominal tensile fracture strain23°CISO 527-221 %
bending strength23°CISO 17872.0 MPa
flammabilityTest ConditionTest MethodASAHI JAPAN/XYRON™ 340W
UL flame retardant rating1.5mmUL 94V-2
physical property Test ConditionTest MethodASAHI JAPAN/XYRON™ 340W
Shrinkage rate2.00mm内部方法0.50to0.70 %
Water absorption rate23°C,24hrISO 620.10 %
densityISO 11831.08 g/cm³
Thermal performanceTest ConditionTest MethodASAHI JAPAN/XYRON™ 340W
Heat distortion temperature1.8MPa,未退火,HDTASTM D648100 °C
Linear coefficient of thermal expansionMD:-30到65°CISO 11359-27.5E-05 cm/cm/°C
Heat distortion temperature1.8MPa,未退火,HDTISO 75-2/A94.0 °C