Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.03 g/cm³ |
| Melt volume flow rate | | ISO 1133 | 14.0 cm³/10min |
| density | | ISO 1183 | 1.03 g/cm³ |
| Melt volume flow rate | | ISO 1133 | 14.0 cm³/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| ball-indentation hardness | | ISO 2039-1 | 59.0 MPa |
| ball-indentation hardness | | ISO 2039-1 | 59.0 MPa |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2/1 | 3500 MPa |
| tensile strength | Yield | ISO 527-2/50 | 45.0 MPa |
| tensile strength | Break | ISO 527-2/5 | 55.0 MPa |
| Tensile strain | Yield | ISO 527-2/50 | 3.0 % |
| Tensile strain | Break | ISO 527-2/5 | 3.4 % |
| Flexural modulus | | ISO 178 | 4010 MPa |
| bending strength | | ISO 178 | 84.9 MPa |
| Tensile modulus | | ISO 527-2/1 | 3500 MPa |
| tensile strength | Yield | ISO 527-2/50 | 45.0 MPa |
| tensile strength | Break | ISO 527-2/5 | 55.0 MPa |
| Tensile strain | Yield | ISO 527-2/50 | 3.0 % |
| Tensile strain | Break | ISO 527-2/5 | 3.4 % |
| Flexural modulus | | ISO 178 | 4010 MPa |
| bending strength | | ISO 178 | 84.9 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 4.1 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/1eA | 5.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 25 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 30 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 25 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 30 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/1eA | 4.1 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/1eA | 5.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | 1E+13 ohms |
| Surface Resistivity | | IEC 60093 | 1E+13 ohms |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/A | 119 °C |
| Heat distortion temperature | | ISO 75-2/B | 155 °C |
| Heat distortion temperature | | ISO 75-2/A | 119 °C |
| Heat distortion temperature | | ISO 75-2/B | 155 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare