Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ISO 1133 | 6.0 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ISO 868 | 41 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| gloss | | ASTM D2457 | 47 |
| Haze ratio | | ASTM D1003 | 8.0 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ISO 527-2 | 8.00 Mpa |
| Tensile strain | | ISO 527-2 | 500 % |
| Flexural modulus | | ISO 178 | 220 Mpa |
| film | Test Condition | Test Method | Test Result |
|---|
| elongation | | ISO 527-3/500 | 890 % |
| film thickness | | | 50 µm |
| Tensile modulus | | ISO 527-3/25 | 125 Mpa |
| Tensile modulus | | ISO 527-3/25 | 110 Mpa |
| tensile strength | | ISO 527-3/500 | 8.00 Mpa |
| tensile strength | | ISO 527-3/500 | 8.00 Mpa |
| tensile strength | | ISO 527-3/500 | 30.0 Mpa |
| tensile strength | | ISO 527-3/500 | 24.0 Mpa |
| elongation | | ISO 527-3/500 | 26 % |
| elongation | | ISO 527-3/500 | 33 % |
| elongation | | ISO 527-3/500 | 990 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 50.0 °C |
| vicat | | ISO 306/A50 | 89.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.