TPO C200F LYONDELLBASELL HOLAND
Hifax
chip、Bag、film、Laminate
High toughness、high definition、Low temperature toughness
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | LYONDELLBASELL HOLAND/C200F |
|---|---|---|---|
| Shore hardness | 邵氏D | ISO 868 | 41 |
| film | Test Condition | Test Method | LYONDELLBASELL HOLAND/C200F |
|---|---|---|---|
| elongation | MD:断裂,50µm,铸造薄膜 | ISO 527-3/500 | 990 % |
| tensile strength | MD:屈服,50µm,铸造薄膜 | ISO 527-3/500 | 8.00 Mpa |
| Tensile modulus | MD:50µm,铸造薄膜 | ISO 527-3/25 | 125 Mpa |
| tensile strength | MD:断裂,50µm,铸造薄膜 | ISO 527-3/500 | 30.0 Mpa |
| elongation | TD:屈服,50µm,铸造薄膜 | ISO 527-3/500 | 33 % |
| Tensile modulus | TD:50µm,铸造薄膜 | ISO 527-3/25 | 110 Mpa |
| film thickness | 50 µm | ||
| tensile strength | TD:屈服,50µm,铸造薄膜 | ISO 527-3/500 | 8.00 Mpa |
| elongation | TD:断裂,50µm,铸造薄膜 | ISO 527-3/500 | 890 % |
| tensile strength | TD:断裂,50µm,铸造薄膜 | ISO 527-3/500 | 24.0 Mpa |
| elongation | MD:屈服,50µm,铸造薄膜 | ISO 527-3/500 | 26 % |
| Mechanical properties | Test Condition | Test Method | LYONDELLBASELL HOLAND/C200F |
|---|---|---|---|
| Tensile strain | 断裂 | ISO 527-2 | 500 % |
| Flexural modulus | ISO 178 | 220 Mpa | |
| tensile strength | 屈服 | ISO 527-2 | 8.00 Mpa |
| optical performance | Test Condition | Test Method | LYONDELLBASELL HOLAND/C200F |
|---|---|---|---|
| Haze ratio | 50.0µm,铸造薄膜 | ASTM D1003 | 8.0 % |
| gloss | 45°,50.0µm,铸造薄膜 | ASTM D2457 | 47 |
| physical property | Test Condition | Test Method | LYONDELLBASELL HOLAND/C200F |
|---|---|---|---|
| melt mass-flow rate | 230°C/2.16kg | ISO 1133 | 6.0 g/10min |
| Thermal performance | Test Condition | Test Method | LYONDELLBASELL HOLAND/C200F |
|---|---|---|---|
| vicat | ISO 306/A50 | 89.0 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 50.0 °C |